全球鋼材百科網(wǎng)
F593 431簡介

牌號 F593 431
美國UNS S43100
對應標準 ASTM F593-2017
不銹鋼螺栓、六角螺釘和螺柱標準規(guī)范
Standard specification for stainless steel bolts, hex cap screws, and studs
歸類 馬氏體不銹鋼
F593 431 化學元素成分含量(%)
成分 C Si Mn P S Cr Ni
最小值 - - - - - 15 1.25
最大值 0.2 1 1 0.04 0.03 17 2.5
碳當量計算
F593 431 機械性能
公稱直徑
inch
試樣		 熱處理或狀態(tài)
抗拉強度
σb
ksi 		屈服點
σs
ksi 		斷后伸長率或延伸率
δ
% 		硬度
HBW
1/4 ~ 1-1/2 (全尺寸) H 125~150 ≥100 HR (C25~32)
1/4 ~ 1-1/2 (全尺寸) HT 180~220 ≥140 HR (C40~48)
1/4 ~ 1-1/2 (機加工) H ≥125 ≥100 ≥15
1/4 ~ 1-1/2 (機加工) HT ≥180 ≥140 ≥10
注1： “全尺寸”指的拉力測試試件是使用前的狀態(tài)未經(jīng)改變的完整的緊固件產(chǎn)品。
注2：A——Machined from annealed or solution-annealed stock thus retaining the properties of the original material, or hot-formed and solution-annealed.
AF——Headed and rolled from annealed stock and then reannealed.
AH——Solution annealed and age-hardened after forming.
CW——Headed and rolled from annealed stock thus acquining a degree of cold work; sizes 0.75 in. and larger may be hot worked and solution-annealed.
H——Hardened and tempered at 1050°F (565℃) minimum.
HT——Hardened and tempered at 525°F (274℃) minimum.
SH——Machined from strain hardened stock or cold-worked to develop the specified properties.
1 近似對照表 馬氏體不銹鋼
中國 中國臺灣 日本 韓國 美國 國際標準組織 德國 法國 歐標 俄羅斯 瑞典 英國
GB ISC CNS JIS KS ASTM UNS ISO 數(shù)字牌號 DIN EN/DIN W-Nr. NF EN/NF EN 數(shù)字牌號 GOST SS BS EN/BS
14Cr17Ni2
(1Cr17Ni2)
17Cr16Ni2 		S43110
/
S43120 		431 SUS 431 STS 431 431 S43100 X17CrNi 16-2 4057-431-00-X X20CrNi 17-2
(X22CrNi 17) 		1.4057 Z15CN 16-02 X17CrNi 16-2 1.4057 14Х17Н2 2321 431S29
2 近似對照表 馬氏體型耐熱鋼
中國 中國臺灣 日本 韓國 美國 德國 法國 歐標 俄羅斯 瑞典 英國
GB ISC CNS JIS KS ASTM UNS DIN EN/DIN W-Nr. NF EN/NF EN 數(shù)字牌號 GOST SS BS EN/BS
14Cr17Ni2
(1Cr17Ni2) 		S43110 431 SUS 431 STS 431 431 S43100 X20CrNi 17-2
(X 22CrNi 17) 		1.4057 Z15CN 16-02 X17CrNi 16-2 1.4057 14Х17Н2 2321 431S29
全球鋼材百科網(wǎng)